Smooth HDPE Geomembrane
| Model: | - |
|---|---|
| Brand: | TIANHE brand |
| Origin: | Made In China |
| Category: | Chemicals / Plastic Materials |
| Label: | HDPE , Geomembrane , Smooth |
| Price: |
-
|
| Min. Order: | - |
Product Description
(HDPE)Geomembrane
Specification: Width: 2000-7000 mm Thickness: 0.75-3.0 mm
Standard: GRI-GM13
TIANHE brand HDPE Geomembrane select quality original polyethylene resin. We use the most advanced internations of Italy Automated production Equipment, after a three-layer co-extresion technology made. All products are based on America GRI and ASTM testing standards for the implementation of the production, completes pecifications and superior quality.
Usage:Landscape Works :artificial lake,ponds ,reservoirs,golf course substretes,revetment works,etc.
Sanitation Project :Life of landfill, sewage treatment toxic and hazardous compounds disposal sites storage of dangerous goods, construction and blasting garbage, etc.
Water Conservancy: Rivers, lakes water reservoir dam seepage control and stopping leaks and strengthened and the drains impermemeable, vertical wall, revetment works,etc.
Mining Chemicalplant: chemicalpiant,oil refineries,gasoline storage tanks impervious chemical reaction tanks, sedimentation pond liners,second liner,etc.
ConstructionProjects: subwayconstruction,building underground engineering and reservoir on the roof,the roof garen impermeable ,sewage pipe lining,etc.
Aqucaulture: ponds,the shrimp pond liners,sea cucumbers circle revetment etc:
Agricutural Engineering: reservoir,drinking water tanks,water storage pound the irrigation system impervious.
Salt Works plant crystallization pool,planted brine pool,salt membrane,and pool plastic memnrane aircraft.
Table 1(b)High Density Polyenthlene (HDPE) Geomembrane –Smooth
|
Properties
|
Test
Method
|
Test Value
|
Testing Frequency
(minimum)
|
|||||||
|
0.50mm
|
0.75 mm
|
1.00mm
|
1.25 mm
|
1.50mm
|
2.00mm
|
2.50mm
|
3.00mm
|
|||
|
Thickness-mils(min.ave.) lowest individual of 10 values
|
D5199
|
nom.(mil)-10%
|
nom.(mil)-10%
|
nom.(mil)
-10%
|
nom.(mil)
-10%
|
nom.(mil)
-10%
|
nom.(mil)
-10%
|
nom.(mil)
-10%
|
nom.(mil)
-10%
|
each roll
|
|
Density (min.)
|
D1505/D 792
|
0.940g/cc
|
0.940g/cc
|
0.940g/cc
|
0.940g/cc
|
0.940g/cc
|
0.940g/cc
|
0.940g/cc
|
0.940g/cc
|
90,000kg
|
|
Tensile Properties (1) (min.ave.)
yield strength
break strength
yield elongation
break elongation
|
D6693
Type IV
|
7kN/m
13kN/m
12%
700%
|
11kN/m
20kN/m
12%
700%
|
15kN/m
27kN/m
12%
700%
|
18kN/m
33kN/m
12%
700%
|
22kN/m
40kN/m
12%
700%
|
29kN/m
53kN/m
12%
700%
|
37kN/m
67kN/m
12%
700%
|
44kN/m
80kN/m
12%
700%
|
9,000kg
|
|
Tear Resistance (min.ave.)
|
D1004
|
62N
|
93N
|
125N
|
156N
|
187N
|
249N
|
311N
|
374N
|
20,000kg
|
|
Puncture Resistance (min.ave.)
|
D4833
|
160N
|
240N
|
320N
|
400N
|
480N
|
640N
|
800N
|
960N
|
20,000kg
|
|
Stress Crack Resistance (2)
|
D5397
(App.)
|
300hr.
|
300hr.
|
300hr.
|
300hr.
|
300hr.
|
300hr.
|
300hr.
|
300hr.
|
per each formulation
|
|
Carbon Black Content - %
|
D1603 (3)
|
2.0-3.0%
|
2.0-3.0%
|
2.0-3.0%
|
2.0-3.0%
|
2.0-3.0%
|
2.0-3.0%
|
2.0-3.0%
|
2.0-3.0%
|
9,000kg
|
|
Carbon Black Dispersion
|
D5596
|
（1）
|
（1）
|
（1）
|
（1）
|
（1）
|
（1）
|
（1）
|
（1）
|
20,000kg
|
|
Oxidative Induction Time (OIT) (min. ave.) (5) (a) Standard OIT. Or(b)High Pressure OIT
|
D3895
D5885
|
100 min.
400 min.
|
100min.
400min
|
100min.
400min
|
100min.
400min
|
100min.
400min
|
100min.
400min
|
100min.
400min
|
100min.
400min
|
90,000kg
|
|
Oven Aging at 85 ℃(5), (6)
(a) Standard OIT (min. ave.) - % retained after 90 days or (b) High Pressure OIT (min. ave.) - % retainedafter 90 days UV esistance (7)
|
D5721
D3895
D5885
|
55%
80%
|
55%
80%
|
55%
80%
|
55%
80%
|
55%
80%
|
55%
80%
|
55%
80%
|
55%
80%
|
per each formulation
|
|
(a) Standard OIT (min. ave.) or(b) High Pressure OIT (min. ave.) - % retained after 1600 hrs (9)
|
D3895
D5885
|
N.R.(8)50%
|
N.R.(8)50%
|
N.R.(8)50%
|
N.R.(8)50%
|
N.R.(8)50%
|
N.R.(8)50%
|
N.R.(8)50%
|
N.R.(8)50%
|
per formulate
|
(1)Machine direction (MD) and cross machine direction (XMD) average values should be on the basis of 5 test specimens each direction
Yield elongation is calculated using a gage length of 33 mm
Break elongation is calculated using a gage length of 50 mm
(2)The yield stress used to calculate the applied load for the SP-NCTL test should be the manufacturer mean value via MQC testing.
(3)Other methods such as D 4218 (muffle furnace) or microwave methods are acceptable if an appropriate correlation to D 1603 (tube furnace) can be established.
(4)Carbon black dispersion (only near spherical agglomerates) for 10 different views:
9 in Categories 1 or 2 and 1 in Category 3
(5)The manufacturer has the option to select either one of the OIT methods listed to evaluate the antioxidant content in the geomembrane.
(6)It is also recommended to evaluate samples at 30 and 60 days to compare with the 90 day response.
(7)The condition of the test should be 20 hr. UV cycle at 75 followed by 4 hr. condensation at 60℃ .
(8)Not recommended since the high temperature of the Std-OIT test produces an unrealistic result for some of the antioxidants in the UV exposed samples.
(9)UV resistance is based on percent retained value regardless of the original HP-OIT value.
Member Information
| Shandong Tianhe Plastic Co.,Ltd | |
|---|---|
| Country/Region: | Shan Dong - China |
| Business Nature: | Manufacturer |
| Phone: | 86-0533-7118378 |
| Contact: | Mandy (saler) |
| Last Online: | 21 Feb, 2019 |