PRODUCT OVERVIEW

LH-Silicones RTV M 20 are tin-cured silicone rubber two components that have exceptional tear strength and working properties and library life which cured overnight at room temperature with low shrinkage to a strong,flexible silicone rubber. Also,reproduce the finest detail and are suitable for a variety of industrial and art related.

 Applications

 making molds for reproducing prototypes, furniture, sculpture and architectural elements with a variety of materials including wax, gypsum, low melt alloys/metals and urethane, polyester resins:

 TECHNICAL PROPERTIES

Appearance (component A)                           : White                             Component B (Hardner) : clear liquid

Viscosity (cps)                                               : 20000(at +23°C)                         

Mixing ratio (mould rubberA+B Harder)         : 100 : 2.5 parts in weight

Specific gravity                                              : 1.10  (at + 23°C))

Hardness (Shore A) At 2mm cured                : 22

Tensile Strength (MPA)                                 : 2.8      

Tear strength ( KN/M)                                   : 2.0

After addition of a catalyst

RTV M 20                                                      100Parts

Catalyst CA-22                                             2.5Part

Pot life of the catalyed mix(23°C, approx)   25minutes

Demould time           (23°C, approx)   4 hours

After addition of a catalyst CA-35

TV M 20                                                         100Parts

Catalyst CA-35                                             4-5Part

Pot life of the catalyed mix(23°C, approx)    60minutes

Demould time           (23°C, approx)    8hours

IMPORTANT: .If there is any question about the effectiveness of products agent combination, a small-scale test should be made on an identical surface for trial. Increase catalyst will caused cured rubber become crispy.


for any details information please contact shgslsl at 21cn dot com,

~Nancy xie
 lianhuan group limited

Phone:0086 13699849627
 Skype:nancyxie2007 

Http://www.lhsilicone.com