The properties of the products

Appearance (component A)                        Translucent          Component B (curing agent)  clear liquid

Viscosity (cps)                                              95000(at +23°C)                          800

Mixing ratio (mould rubberA+B Harder)     10 : 1 parts in weight

Hardness (Shore A) At 2mm cured               38

Tensile Strength kg/cm²(MPA)                     10     

Tear strength kgf / cm ( KN/M)                    14

Elongation(%)                                                 500

Prepare methods:

    1.      Mixed Color master batch: Using it when needing various colors. Adding 0.2% of total amount material.

    2.      Mixed 10% CATATLYST curing agent into small amount of silicone ink(90%).

    3.      The curing agent should be mixed very well,Otherwise,some parts won’t be cured.

    4.      could use thinner for decrease the viscosity,over 15% of thinner, the abrasiveness, durability and adhesion force will be reduce. There tested before production is required.

Drying methods  

1. According to different thickness of silicone ink, the curing time is also different. Normal situation for mixing Part A Part B 10to 1 curing time is 50seconds with the temperature of 150°C(polycondesation cured process).

2. When the room temperature is above 25°C (humidity 50%), room temperature cure can be carried out under summer condition

3.Color master batch Using it when needing various colors.                    

 for any details information please contact shgslsl at 21cn dot com,

~Nancy xie
 lianhuan group limited

Phone:0086 13699849627
 Skype:nancyxie2007 