Laminated Composite Filter Media is compounded by ultrasonic melting and hot-melf fibre adhesive technology to bond different layers of material together.To enhance physical or chemical performance of filtration media which can be widely used in pleatable filter.

Product Performance:
1.Flat appearance and high intensity
2.High stiffness,be easy to pleated.
3.At the condition of reaching the same efficiency,the resistance of the material decrease by 20%.
4.Own the advantage of great dust capacity and extending the life-span of filter.

Product Technical Datas:

Type	Basic W. g/m2	Thickness mm	Stiffness mg	0.38µm@85L/min-dm2		Application	Remarks
				Resistance Pa	Efficiency %
FC-45	115	0.85	1000	15	48%	F5	PP and PET  ultrasonic melting
FC-65	120	0.88	1200	18	68%	F6
FC-85	130	0.91	1500	21	80%	F7
FC-95	140	0.93	1800	35	85%	F8
FC-98	145	0.95	1800	40	90%	F9~Y10
FC-C85	110	0.78	1200	45	92%	Y10~Y11	PP and PET  ultrasonic melting or  hot-melt fiber adhesive
FC-C195	115	0.80	1600	50	99%
FC-C295	120	0.82	1650	50	99.8%	Y12
FC-C395	130	0.85	1700	65	99.98%	Y13