1.2379 Tool Steel
|
Standards |
DIN |
AISI |
JIS |
ГОСТ |
|
X155CrVMo12-1 |
1.2379 |
D2 |
SKD11 |
Х12МФ |
ALTA SPECIAL STEEL supply DIN 1.2379 / AISI D2 in round bar, plate, square, sheet and block.
Chrome-molybdenum-vanadium steel with big hardenability for hardening in oil and in air, especially high resistance to the wear (higher than by 1.2080), good cutting power, very good firmness in the pressure, lower toughness (but higher than by 1.2080). This steel shows good dimensional stability at the heat treatment, suitable for hardening to the secondary hardness (the possibility of nitriding). Further the steel is very difficult to sharpen, it works at the heat with difficulties and has a rather difficult workability in the annealed state.
We welcome your inquiries for tool steel, please contact us for quotation sales@altaspecialsteel.com
_________________________________________________________________________________________
Chemical Composition
|
C |
Si |
Mn |
P |
S |
Cr |
Mo |
V |
|
1.45-1.60 |
0.10-0.40 |
0.15-0.45 |
≤0.030 |
≤0.030 |
11.0-13.0 |
0.70-1.00 |
0.70-1.10 |
Product Range
Round bars : Dia 8mm - 450mm
Flat bars : Thick 8mm - 400mm, width up to 810mm
_________________________________________________________________________________________
Applications : cutting, punching, stamping tools, shear blades, thread rolling dies, drawing and bending tools, flanging and straightening rolls, deep drawing tools, plastic mould for abrasive polymers, cold extrusion dies, dawing dies etc.
_________________________________________________________________________________________
Heat Treatment
|
Way |
Temperature[℃] |
Remark |
|
Forging |
850 - 1050 |
|
|
Soft annealing |
800 - 850 |
Max. 250HB after annealing |
|
Quenching |
1000 - 1090 |
Cool in oil, air or salt bath at the temperature of about 500-550°C |
|
Tempering |
150 - 540 |
|
|
℃ |
100 |
200 |
300 |
400 |
500 |
600 |
|
HRC |
63 |
61 |
59 |
58 |
57 |
52 |