TYPICAL PROPERTIES OF SIL-PAD 900S
|
| PROPERTY IMPERIAL＆#118alue METRIC＆#118alue TEST METHOD |
| Color Pink Pink Visual |
|
Reinforcement Carrier Fiberglass Fiberglass ─
|
|
Thickness(inch)/(mm) 0.009 0.229 ASTM D374
|
|
Hardness(Shore A) 92 92 ASTM D2240
|
|
Elongation(%45ºto Warp & Fill) 20 20 ASTM D412
|
|
Tensile Strength(psi)/(Mpa) 1300 9 ASTM D412
|
|
Continuous Use Temp(ºF)/(℃) -76 to 356 -60 to 180 ─
|
| ELECTRICAL |
| Dielectric Breakdown Voltage(Vac) 5500 5500 ASTM D149 |
| Type 3 Electrodes 8300 8300 ASTM D149 |
|
Dielectric Constant(1000Hz) 6.0 6.0 ASTM D150
|
|
Volume Resistivity(Ohm-meter) 1010 1010 ASTM D257
|
|
Flame Rating 94V-O 94V-O U.L
|
| THERMAL |
|
Thermal Conductiviy(W/m-K) 1.6 a1.60.61 ASTM D5470
|
| THERMAL PERFORMANCE vs PRESSURE |
| Pressure(psi) 10 25 50 100 200 |
| TO-220 Thermal Performance(℃/W) 3.96 3.41 2.90 2.53 2.32 |
| Thermal Impedance(℃-in2/W) (1) 0.95 0.75 0.61 0.47 0.41 |
|
1）The ASTM5470(Bergquist modified)test fixture was used and the testsample was conditioned at 70℃prior to test.Therecorded ＆#118alue includes interfacial thermal resistance.These ＆#118alue are provided for referrnce omly.Actual application performance isdirectly related to the surface roughness.flatness an d pressure applied.
|