SILICONE GEL

DESCRIPTION:

The silicone gel is a low viscosity, with a viscous, gel-like transparent, two component additionl molding silicone gels may be cured at room temperature, can also be heated to curing, the higher the temperature the curing sooners. This product does not produce any by-product in the curing reaction, may be applied to the surface of a PC (Poly-carbonate), PP, ABS, PVC and other materials and metals. For electronic accessories insulation, waterproof and fixed. In full compliance with the EU ROHS Directive requirements.

 

USEAGE:

Silicone gel for the body shape, sexual organs, chest pads, shoulder pads, patch, non-slip mats, floor mats, flexible silicone rubber products can also be used for the simulation of human facial silicone mold is mainly used for human facial imitation human limb shape the same type. changing shape, soft touch.

 

CHARACTERISTICS: 

This gel can be flexible for long-term in the temperature range of -65 ~ 200 ℃ , it has excellent electrical properties and chemical stability,Water resistance, ozone resistance, resistance to weathering, water-repellent, moisture-proof, shock-proof, non-corrosive, and physiologically inert, non-toxic, odorless, easy-to-perfusion,  Can deep vulcanization, low linear shrinkage, simple operation.

 

Method Of Operation:

1.Before mixing, first put the component A and component B in each container  and stir evenly.

2.Mixing, should comply with the component A: component B = 1:1 ratio.

3 Deforming when useing depend on the fact. A, B mixture was stirred uniformly placed in a vacuum container, deforming under 0.08MP for 5 minutes,so that can prime used.

4Addition molding silicone gel before and after curing should be kept to the temperature given in the technical parameters , to maintain the appropriate curing time. If the application is thick, the curing time may be exceeded. Room temperature or heat cure both can be cured. The curing speed is affected by  the curing temperature, and it need a long time to be cured in the winter, it is recommended to adopt the heating curing at 80 to 100 °C, cured for 20 minutes, under room temperature , curing typically takes about 8 hours.

The following substances may hinder the curing or bring uncured phenomenon, it is better to clearing the application site or take some simple experimental verification  when necessary.

① Incompletely cured condensation type silicone

② Amine  curable epoxy resin

③ White wax welding processing (solder flux)

 

Packaging:

A component 20or200 KG / DRUM

B component 20or200 KG / DRUM, sealed by non-dangerous goods transportation, room temperature storage period of 2 years

 

Note: This silicone can not contact any other condensation-type silicone, otherwise it would cause the curing agent poisoning, caused silicone can't curing phenomenon. Water ,impurity, Organic bismuth catalyst,acid, alkali and other organic contain sulfur, phosphorus, nitrogen may affect the curing of the glue, can't be mixed or exposure to these substances when useing.