Descripation:

 

RTV-2 life casting silicone rubber is two-component addition cure heating or room temperature vulcanizing silicone rubber ,the product, which is colorless or skin-colored oily liquid and becomes soft elastic material after vulcanization, can be used for making soft silicone rubber.

 

Characteristical:

 

• Easy to use                      

• Use platinum catalyst 

• High degree of precision in reproduction

• High transparency,almost non shrinkage

• Good heat stability and weatherability(resist -60 to 250°C)

• Low compression set,grat stability and ability to resist extreme temperatures of heat and cold.

 

 

Application:

 

• Paster

• Traction

• Sex toys

• Body organs

• Shoulder pads

• Body breast enhancers

• Other soft silicone products

 

 

Parameter:

 

Catalyst

 

 

Working and cure times at room temperature (25°C)Catalyst	Appearance	Base/catalyst mixing ratio by weight	Pot life Time mins	De-mold Time
T02	clear	1:1	30-40mins	4-6hrs
T02	clear	1:1	50-60mins	9-10hrs
T02	clear	1:1	90mins	24hrs

 

 

 

Silicone

 

Characteristical before curing			Characteristical after curing
Item NO.	Appearance	Viscosity	Hardness	Tear strength	Tensile Strength(Mpa)	Elongation break (%)	Linear Shrinkage(%)
		Mpa.s	Shore A	(KN/m)
RTV1205	translucent	4000±2000	5±2	7±2	>4.0	410	≤0.1

 

 

 

 

How to make mold?

 

 

1.Mixing

Please weight 1 Part A base and 1 parts Catalyst in a clean container.Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until part B completely dispersed in the base. Hand or mechanical mixing can be used,but do not for an extended period of time or allow the temperature to exceed 35°C. Mix suitably small quantities to ensure thorough mixing of base and catalyst.

It is strongly recommended that entrapped air be removed in a vacuum chamber,allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum,the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

 

2.Pouring the mixture and curing

Pour the mixed Part A base silicone and part B catalyst as soon as possible onto the original,avoiding air entrapment.The catalyzed material will cure to a flexible rubber within 24 hours(or faster by different mixing ratio or room temperature).

 

Storage:

 

When stored at or below 30°C in the original unopened containers,SILASTIC Base and catalyst have a usable life of 12 months.from the date of production.After 12 months stock,pls use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again,no influence for other performance.

 