Descripation:

 

Shoe soles silicone rubber is generally named astwo-part silicone rubber that vulcanizes at room temperature.Part A is a flow able liquid,part B is the catalyst.

 

 

Characteristical:

 

• Easy to use                       

• Use platinum catalyst 

• Cures at room temperature within 3-4 hours

• Good tensile and tear strength,low shrinkage
• Good resistance to weather,temperature,aging,acid

• An exceptional fluidity and good operability,easy to remold 

 

 

Application:

 

 

• Shoe molds

• Sand casting

• Sole sampling

• Plaster models

• Simple products

• Products with non-complex patterns

 

 

Parameter:

 

Catalyst

 

 

Working and cure times at room temperature (25°C)Catalyst	Appearance	Base/catalyst mixing ratio by weight	Pot life Time mins	De-mold Time
T01	clear	100:2	30-40mins	14-15hrs
T01	clear	100:3	20-30mins	9-10hrs
T01	clear	100:4	10-20mins	4-5hrs

 

 

 

 

 

Silicone

 

Characteristical before curing			Characteristical after curing
Item NO.	Appearance	Viscosity	Hardness	Tear strength	Tensile Strength(Mpa)	Elongation break (%)	Linear Shrinkage(%)
		Mpa.s	Shore A	(KN/m)
RS17	white	11000±2000	17±2	10±2	>1.8	250	≤0.2

 

 

How to make mold?

 

 

1.Mixing

Please weight 100 Part A base and 2 parts of organic tin catalyst in a clean container.Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until part B completely dispersed in the base. Hand or mechanical mixing can be used,but do not for an extended period of time or allow the temperature to exceed 35°C. Mix suitably small quantities to ensure thorough mixing of base and catalyst.

It is strongly recommended that entrapped air be removed in a vacuum chamber,allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum,the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

 

2.Pouring the mixture and curing

Pour the mixed Part A base silicone and part B organic tin catalyst as soon as possible onto the original,avoiding air entrapment.The catalyzed material will cure to a flexible rubber within 6 hours(or faster by different mixing ratio or room temperature),we advice you de-mold after 24 hours ,it is will improve the replicate times of silicone mold.

 

 

Storage:

 

 

When stored at or below 30°C in the original unopened containers,SILASTIC Base and Catalyst have a usable life of 12 months.from the date of production.After 12 months stock,pls use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again,no influence for other performance.

 

Note:

 

This product is neither tested nor represented as suitable for medical or pharmaceutical uses. Not intended for human injection. Not intended for food use.

 

Packing:

 

 

 

 

Certificate:

 

 

 

 

 

Payment:

 

 

 

 

Shipping:

 

 

 

 

Contact info:

 

Name:Mysinely

Skype:mysinely

E-mail:mysinely(at)rtv-2.net

MSN:mysinely(at)live.com

Web:www.rtv-2.com