Descripation:

 

Electronic potting silicone rubber is generally named astwo-part silicone rubber that vulcanizes at room temperature.Part A is a flow able liquid,part B is the platinum catalyst.

 

Features:

 

• UL 94V-0

• Water proof 

• Good flowability                          

• Inflaming retarding

• Moderate thermal conductivity

• Room temperature or heat accelerated cure                                    

 

Benefits:

 

• Rapid, versatile cure processing controlled by temperature

• Can be considered for uses requiring added flame resistance

 

Composition: 

 

• 1 to 1 Mix Ratio   

• Polydimethylsiloxane

• platinum curing agent

 

 

Applications:

 

Suitable for general potting material for power supplies, connectors, sensors, industrial controls and transformers.

 

Parameter:

 

 

Before curing	Item NO.		RTV-1305
	Appearance		black
	Viscosity Mpa.s	part A	3000
		part B	3400
	Density(g/cm3)	part A	1.35-1.40
		part B	1.38-1.40
	Ratio(part A+part B)		10:1
	Pot life at 25°Cmins		60
	De-molding time at 25°C (H)		24
	De-molding time at 50°C (H)		4-6
	De-molding time at 100°C (H)		1-2
	De-molding time at 150°C (H)		0.5-1
After curing	Hardness Shore A		30-40
	Elongation break%		50-60
	Tear strength(KN/m)		1.8
	Tensile Strength(Mpa)		0.5-1.5
	Volume resistivity/Ω.cm		≥1014
	Break down voltage(kv/mm)		≥15
	Specific inductive  capacity(50Hz)		2.7-3.3
	Dielectric loss factor(50Hz)		≤0.02
	Thermal conductivity		≥0.5

 

 

 

 

How to make mold?

 

1.Mixing

Please weight 1 Part A base and 1 parts of platinum Catalyst in a clean container.Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until part B completely dispersed in the base. Hand or mechanical mixing can be used,but do not for an extended period of time or allow the temperature to exceed 35°C. Mix suitably small quantities to ensure thorough mixing of base and catalyst.

It is strongly recommended that entrapped air be removed in a vacuum chamber,allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum,the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

 

2.Pouring the mixture and curing

Pour the mixed Part A base silicone and part B platinum catalyst as soon as possible onto the original,avoiding air entrapment.The catalyzed material will cure to a flexible rubber within 24 hours(or faster by different mixing ratio or room temperature).

 

 

Storage:

 

When stored at or below 30°C in the original unopened containers,SILASTIC Base and platinum Catalyst have a usable life of 12 months.from the date of production.After 12 months stock,pls use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again,no influence for other performance.

 

 