Descripation:

 

RTV-2 mold making addition silicone rubber is generally named as two-part silicone rubber that vulcanizes at room temperature.Part A is a flow able liquid ,part B is the platinum catalyst.

 

Characteristical:

 

• Easy to use 

• Almost nil shrinkage                      

• Use platinum catalyst 

• Excellent non-stick effect 

• High degree of precision in reproduction
• High dimensional stability over time and non-deformability

• Food grade silicone (environmental,odorless and nontoxic)  

• High resistance to high temperature and aging(resist -60 to 200°C)  

• High chemical resistance to aggressive components of some types of resins
• Good tear strength (this feature ensures higher resistance to wearing and shearing)

 

 

Application:

 

• PU resin casting

• General mold making

• GRC and concrete molding

• Superior manual mold design

• Food grade molding application

• Rapid prototyping(urethane casting/silicone tooling/vacuum casting)

 

 

Parameter:

 

Catalyst

Working and cure times at room temperature (25°C)Catalyst	Appearance	Base/catalyst mixing ratio by weight	Pot life Time mins	De-mold Time
P10	clear	100:10	60mins	24hrs
P11	clear	1:1	30-40mins	24hrs

 

Silicone

 

Characteristical before curing			Characteristical after curing
Item NO.	Appearance	Viscosity	Hardness	Tear strength	Tensile Strength(Mpa)	Elongation break (%)	Linear Shrinkage(%)
		Mpa.s	Shore A	(KN/m)
RTV1311	transparent	15000±2000	10±2	31±2	>2.7	750	<0.1

 

How to make mold?

 

1.Mixing

Please weight 10 Part A base and 1 parts of platinum Catalyst in a clean container.Thoroughly stir Part A base silicone before use, as filler separation may occur upon prolonged storage. Mixing Part A and Part B evenly until part B completely dispersed in the base. Hand or mechanical mixing can be used,but do not for an extended period of time or allow the temperature to exceed 35°C. Mix suitably small quantities to ensure thorough mixing of base and catalyst.

It is strongly recommended that entrapped air be removed in a vacuum chamber,allowing the mix to completely expand and then collapse. After a further 1-2 mins under vacuum,the mix should be inspected and can be used if free of air bubbles. A volume increase of 3-5 times will occur on vacuum de-airing the mixture. So a suitably large container should be chosen.

 

2.Pouring the mixture and curing

Pour the mixed Part A base silicone and part B platinum catalyst as soon as possible onto the original,avoiding air entrapment.The catalyzed material will cure to a flexible rubber within 24 hours(or faster by different mixing ratio or room temperature).

 

 

Storage:

 

When stored at or below 30°C in the original unopened containers,SILASTIC Base and platinum Catalyst have a usable life of 12 months.from the date of production.After 12 months stock,pls use the Stir to mixing the Part A silicone for some mins, then the silicone can be use again,no influence for other performance.

 

 