Resin crafts mold making rtv silicone rubber 

Product Description

Product Description

• Place of Origin:Wuhan, China (Mainland)
• Brand Name:Silicone xilikang
• Model Number: M625# M620# M630# RTV-2 
• Color:red/white/yellow/blue
• Application:Mold making silicone rubber
• H.S. code:39100000
• Shelf life:12 months
• Appearance:Liquid
• Catalyst:4% for free of charged
• Molding method:Pouring / brushing
• MOQ:100kgs
• Sample:Free
• Package:Vacuum packing

Packaging & Delivery

Specifications

rtv silicone rubber for resin crafts mold making,high temperature,and expansion,silicon flexible mold,easy demold 

Product Description

resin crafts mold making rtv silicone rubber 

[1] resin crafts mold making rtv silicone rubber instruction:

rtv silicone rubber for resin crafts mold making are generally named as two-part room temperature sulfurated silicone rubber, which features an exceptional fluidity and good operability. When mixed with 2-3% curing agent, they can still be operated within 30 minutes, but will be formed after 2-3 hours. With resistance to deformation, high temperature, acid and alkali, and expansion, silicon flexible molds are used for mold duplication and delicate mold making for poli crafts, resin crafts lighting and candle crafts.

[2] resin crafts mold making rtv silicone rubber application

rtv silicone rubber for resin crafts mold making mainly applicable to make the silicone mould for cultural relic duplication,architectural decoration, resin crafts, lighting ornaments, statues, prefabricated concrete, rosettes, cornices, fountains and garden articles, sanitary fixtures, decorative pottery, giftware, industrial equipment, decorative candles, gaskets, mechanical components, but also soles for footwear, archaeological findings or automotive prototypes.

[3] Datesheet of resin crafts mold making rtv silicone rubber 
630# Mainly be used for making various mold which features detailed pattern crafts, plastic , resin products and so on.

Model M630# resin crafts mold making rtv silicone rubber 
Appearance white
Mixing proportion of curing agent(%) 2
Operating time ( hours ) 0.5
Curing time( hours ) 2-4
Hardness (A°) 28-32
Viscosity (CS) 26000-32000
Tensile-strength( kgf /cm2 ) ≥41
Tear-strength (kgf /cm2 ) ≥30

Elongation-break(%) ≥ 470
Retractility(%) ≤0.25
Packing (kg/pail ) 25 or 200 per pail

M628# white, the usage for poly crafts, lighting and candles ,molds in multiple pieces for large products

Model M628# resin crafts mold making rtv silicone rubber 
Appearance white
Mixing proportion of curing agent(%) 2%
Operating time ( hours ) 0.5
Curing time( hours ) 2-4
Hardness (A°) 25-30 
Viscosity (CS) 25000-28000
Tensile-strength( kgf /cm2 ) ≥35
Tear-strength (kgf /cm2 ) ≥25
Elongation-break(%) ≥ 470
Retractility(%) ≤0.25
Packing (kg/pail ) 25,200